2C epoxy primer

Name: 2C epoxy primer
Brand: Würth
SKU: 5866104105

Primer 2C epoxy primer
PRIM-EPOXY-2C-5KG

Art.-no. 5866104105

EAN 4047376455092

All versions

Similar products

Prices for customers after login

2C epoxy primer

Art.-no. 5866104105

Prices for customers after login

Quantity

x 1 pcs

Exclusively for trade customers

Login/Register
Call customer service:

Primer that is resistant to chemicals with excellent adhesion and outstanding corrosion protection properties

High protection against corrosion

Suitable for electrostatic application

Excellent chemical and mechanical resistance

Can be used for insulation purposes on thermoplastic surfaces

Permissible maximum VOC content: 540 g/l of product category 2 (e) of the German Ordinance on Solvent-Based Paints and Lacquers (ChemVOC FarbV). Max. VOC content: 565 g/l

Solids content of base material in %: 69.8

Available colours: FC 0006 = light grey

Notice

The surface must have the correct pre-treatment depending on the surface. Not suitable for powder coatings (temperatures too high)

The usage instructions are recommendations based on the tests we have conducted and are based on our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee the consistent quality of our products. We reserve the right to make technical changes and carry out further development.

Product information

Würth Catalogue

Datasheets(X)

Safety data sheet

Certificates/ Documents

Application area

As a high-quality primer in machine and boat construction, in agriculture, and for chemical transporters. Ideal primer for aluminium structures, e.g. in the bus sector, because it can be coated with filler. Surfaces: Painted surfaces, bare sheet steel, filled surfaces, can be coated with polyester fillers once cured. Reworking with PU sealants, e.g. Bond+Seal Can be painted over with all commercially available paints. Available colours: FC 0006 = light grey

Instructions

Mixture by weight: 5:1 with epoxy hardener with universal thinner. Diluting adjustment depending on coat thickness up to 25 vol.%. Application tools: Brush, roller or paint spray gun, minimum nozzle size 1.6 mm

Can be painted over with all 1-component and 2-component products, at the earliest after 1 hour, at the latest after 24 hours, as sanding must be repeated after 24 hours.

Weight of content	5 kg
Chemical basis	2-methoxy-1-methylethyl acetate
Available colours	FC 0006
Colour	Light grey
Conditions for drying time	at 20°C
Max. processing temperature	30 °C
Density	1.556 g/cm³
Max. temperature resistance	150 °C
Max. short-term temperature resistance	180 °C
Density conditions	at 20°C
VOC concentration (CH)	540 g/l
Min. processing temperature	10 °C
Min. proportion of solids	68 %
Max. proportion of solids	72 %
Shelf life from production	36 Month

Suitable glove:

Product

Description

Chemical protective glove, Butyl

Description:

Permeation level: 5

Gas-tight and resistant to exhaust gases produced by combustion processes

Nitrile chemical protective glove Long, heavy-duty design

Description:

Permeation level: 1

Permeation is the process by which a chemical moves through the material of a protective glove on a molecular level. The time from the initial contact between the chemical and the glove to the permeation of the material is the breakthrough time.

Measured breakthrough time

Permeation level

< 10 min

≥ 10 min

≥ 30 min

≥ 60 min

≥ 120 min

≥ 240 min

≥ 480 min

Important information:

The information given is based on experience and laboratory conditions and is designed as a guide. However, the actual suitability of a glove depends on the individual conditions of its use and must be confirmed by an appropriate test under operational conditions. Given the variety of materials and chemicals used, the possibility of incompatibility or usage problems for the wearer cannot be excluded in individual cases. We would be happy to advise you about optimum solutions.