2C soft solder replacement
2C-tin-solder replacement
TINSLDRREPL-2C-180ML
Register now and access more than 125,000 products
Alternative to hot soldering
No open flames required
Saves time
No removal of airbags, plastic parts, textiles, tank etc.
No damage to painted surfaces, cavity conservation and joint seals
- Good adhesion including on aluminium, iron and steel
- Can be painted over
- Dust-free sanding
- Optimum flexural strength
- Resistant to petrol, diesel and diluted acids
- Does not shrink
- Lead-free
Suitable for use with any commercially available 310 ml cartridge gun (mechanical/electrical/compressed air) Due to the high viscosity, we recommend the use of cordless or compressed air application guns.
Store unopened in a dry place at 10-35°C. Keep away from direct sunlight.
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
Datasheets(X)
For work on metal surfaces on bodywork, particularly for modelling and touching up repair sites.
Thoroughly clean and sand the area to be treated. Remove any old uncured coats of paint and primer. Before use, press on the cartridge until both components are extruded uniformly. Then attach the mixer and discard the first 5 cm of the bead. Now apply the 2-component soft solder replacement and distribute outwards with a spatula starting from the damaged area. Ready to sand with minimal dust after 4-5 hours at 20°C (or approximately 20-30 minutes at 60°C).
Contents | 180 ml |
Weight of content | 320 g |
Conditions for VOC concentration | ChemVOCFarb |
Chemical basis | Epoxy resin |
Colour | Silver grey |
Hardener content | 50 % |
Density | 1.772 g/cm³ |
Density conditions | at 20°C |
Max. working life | 30 min |
Min. working life | 15 min |
Conditions for working life | at 20°C |
Conditions for drying time | at 20°C and 50% relative humidity |
Min. drying time | 4 h |
Max. drying time | 5 h |
Min. processing temperature | 10 °C |
Max. temperature resistance of the hardened material | 100 °C |
Max. permissible VOC concentration | 250 g/l |
Max. VOC concentration | 0 g/l |
Shelf life from production | 12 Month |
Last viewed
Hexagonal bolt with shank
Electromagnetic hold-open device, single-leaf Non-hinge side With GTS 640 G and integrated smoke detector
GEFU® thread-rolling screw With Taptite 2000® thread, flat head with hexalobular drive
Hexagon Socket Head Cap Screw ISO 4762/DIN 912, steel 10.9, zinc-plated, blue passivated (A2K)
EPS profile double cylinder
Holder For bottles of polish
Countersunk head screw with nib and nut
Hexagon Socket Head Cap Screw
W-SLB system storage box with coupling function
AW® C 6.3 bit (1/4 inch) with patented AW tip and colour coding