HSCo dovetail milling cutter DIN 1833 D

Name: HSCo dovetail milling cutter DIN 1833 D
Brand: Würth
SKU: 5443600338

Dove. mil. cut. HSCo DIN 1833D Z8-12 45-60° type N
ANGLCTR-DIN1833D-HSCO-D32,0X60°

Art.-no. 5443600338

EAN 4055375875148

All versions

Specification

Recommended for milling construction steels, case-hardened steels and tempering steels with standard strength up to 1,100 N/mm² and for short-chipping non-ferrous metals

Technical information


Product code	1424
Angle (σ)	60 Degree
Diameter (d1)	32 mm
Cutting width (b)	12.5
Shank diameter (d2)	16 mm
Length (l1)	71 mm
Number of cutting edges (Z)	12 PCS
Material to be processed	Steel, Cast metal, Stainless steel, Titanium, Copper, Brass, Plastic
Standards	DIN 1833
Cutting material	HSCo
Surface	Plain
Shank style	Cylindrical DIN 1835-B
Tolerance of cutting edge diameter	js16
Tolerance of shank diameter	h6
Material of sub-group	General structural steels, Non-alloyed tempering steels < 1000 N/mm², Alloyed tempering steels < 1000 N/mm², Nitriding steels < 1300 N/mm², Grey cast iron, Malleable cast iron, Stainless steels < 850 N/mm², Stainless steels > 850 N/mm², Titanium, Titanium alloys, Copper, Brass, Plastics

Legend
E = emulsion		a_e = 0.1xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/t]		a_p = 1.5xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions.

Cutting values for finishing contour
For dia. 16 to dia. 32
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 16 to dia. 19.9	Dia. 20 to dia. 23	Dia. 24 to dia. 31.9	Dia. 32
General structural steels	< 500 N/mm²	E	45	0,030	0,037	0,048	0,068
General structural steels	500-850 N/mm²	E	38	0,026	0,033	0,043	0,059
Carbon steels	< 850 N/mm²	E	38	0,021	0,026	0,030	0,041
Carbon steels	850-1000 N/mm²	E	30	0,021	0,026	0,030	0,041
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,021	0,026	0,030	0,041
	700-850 N/mm²	E	38	0,021	0,026	0,030	0,041
	850-1000 N/mm²	E	30	0,021	0,026	0,030	0,041
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,021	0,026	0,030	0,041
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,024	0,030	0,034	0,046
Unalloyed case-hardening steels	< 750 N/mm²	E	38	0,021	0,026	0,030	0,041
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,021	0,026	0,030	0,041
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,024	0,030	0,034	0,046
Nitriding steels	< 1000 N/mm²	E	30	0,021	0,026	0,030	0,041
Nitriding steels	1000-1200 N/mm²	E	25	0,024	0,030	0,034	0,046
Tool steels	< 850 N/mm²	E	38	0,021	0,026	0,030	0,041
	850-1100 N/mm²	E	25	0,024	0,030	0,034	0,046
	1100-1400 N/mm²	E	20	0,024	0,030	0,034	0,046
High-speed steels	850-1200 N/mm²	E	20	0,024	0,036	0,041	0,054
Wear-resistant constructional steel	1350 N/mm²	E	15	0,024	0,030	0,034	0,046
Spring steels	< 1200 N/mm²	E	15	0,024	0,030	0,034	0,046
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,021	0,026	0,030	0,041
Stainless steels, austenitic	< 700 N/mm²	E	38	0,021	0,026	0,030	0,041
Stainless steels, austenitic	< 850 N/mm²	E	30	0,021	0,026	0,030	0,041
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,024	0,030	0,034	0,046
Cast iron	< 180 HB	-	38	0,021	0,026	0,030	0,041
Cast iron	> 180 HB	-	30	0,021	0,026	0,030	0,041
Nodular graphite, malleable iron	> 180 HB	-	30	0,021	0,026	0,030	0,041
Nodular graphite, malleable iron	> 260 HB	E	25	0,021	0,026	0,030	0,041
Titanium, titanium alloys	< 850 N/mm²	E	20	0,024	0,030	0,034	0,046
Copper, low-alloy	< 350 N/mm²	E	120	0,039	0,047	0,053	0,071
Brass, short-chipping	< 600 N/mm²	-	100	0,039	0,047	0,053	0,071
Brass, long-chipping	< 600 N/mm²	-	100	0,039	0,047	0,053	0,071
Bronze, short-chipping	< 600 N/mm²	-	100	0,039	0,047	0,053	0,071
Bronze, short-chipping	650-850 N/mm²	-	80	0,039	0,047	0,053	0,071
Bronze, long-chipping	< 850 N/mm²	E	80	0,039	0,047	0,053	0,071
Bronze, long-chipping	850-1200 N/mm²	E	65	0,043	0,051	0,058	0,078