HSCo type N double-cut side and face milling cutter DIN 885A - CTR-DIN885A-HSCO-D50X8MM

HSCo type N double-cut side and face milling cutter DIN 885A

Name: HSCo type N double-cut side and face milling cutter DIN 885A
Brand: Würth
SKU: 5443601204

Milling cutter HSCo DIN 885A Z12-20 10° type N
CTR-DIN885A-HSCO-D50X8MM

Art.-no. 5443601204

EAN 4055375881408

All versions

Specification

Recommended for milling structural, case-hardening and heat-treated steels up to 1,100 N/mm² and for short-chipping non-ferrous metals.

Technical information


Product code	3174
Material to be processed	Steel, Cast metal, Stainless steel, Titanium, Copper, Brass, Aluminium, Plastic
Diameter (d1 (js16))	50 mm
Cutting width (b)	8
Cutting depth (a)	11.5 mm
Bore diameter (d2 (H7))	16 mm
Number of cutting edges (Z)	12 PCS
Milling cutter design standard	DIN 885 A
Cutting material	HSCo
Twist angle	10°
Surface	Plain
Tolerance of cutting edge diameter	js16
Tool holding device	With longitudinal groove DIN 138
Material of sub-group	General structural steels, Non-alloyed tempering steels < 1000 N/mm², Alloyed tempering steels < 1000 N/mm², Nitriding steels < 1300 N/mm², Grey cast iron, Malleable cast iron, Stainless steels < 850 N/mm², Stainless steels > 850 N/mm², Titanium, Titanium alloys, Copper, Brass, Aluminium, Plastics

Cutting values for finishing contour
For dia. 50-160
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 50	Dia. 63	Dia. 80	Dia. 100	Dia. 125-160
General structural steels	< 500 N/mm²	E	45	0,057	0,068	0,080	0,091	0,103
General structural steels	500-850 N/mm²	E	38	0,050	0,060	0,070	0,080	0,090
Carbon steels	< 850 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
Carbon steels	850-1000 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
	700-850 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
	850-1000 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,040	0,048	0,056	0,064	0,072
Unalloyed case-hardening steels	< 750 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,040	0,048	0,056	0,064	0,072
Nitriding steels	< 1000 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Nitriding steels	1000-1200 N/mm²	E	25	0,040	0,048	0,056	0,064	0,072
Tool steels	< 850 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
	850-1100 N/mm²	E	25	0,040	0,048	0,056	0,064	0,072
	1100-1400 N/mm²	E	20	0,040	0,048	0,056	0,064	0,072
High-speed steels	850-1200 N/mm²	E	20	0,048	0,058	0,067	0,077	0,086
Wear-resistant constructional steel	1350 N/mm²	E	15	0,040	0,048	0,056	0,064	0,072
Spring steels	< 1200 N/mm²	E	15	0,040	0,048	0,056	0,064	0,072
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
Stainless steels, austenitic	< 700 N/mm²	E	38	0,035	0,042	0,049	0,056	0,063
Stainless steels, austenitic	< 850 N/mm²	E	30	0,035	0,042	0,049	0,056	0,063
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,040	0,048	0,056	0,064	0,072
Special alloys	< 1200 N/mm²	E	15	0,040	0,048	0,056	0,064	0,072
Cast iron	< 180 HB	-	38	0,035	0,042	0,049	0,056	0,063
Cast iron	> 180 HB	-	30	0,035	0,042	0,049	0,056	0,063
Nodular graphite, malleable iron	> 180 HB	-	30	0,035	0,042	0,049	0,056	0,063
Nodular graphite, malleable iron	> 260 HB	E	25	0,035	0,042	0,049	0,056	0,063
Titanium, titanium alloys	< 850 N/mm²	E	20	0,040	0,048	0,056	0,064	0,072
Aluminium, aluminium alloys	< 530 N/mm²	E	400	0,057	0,068	0,080	0,091	0,103
Aluminium, cast aluminium alloys < 10 % Si	< 600 N/mm²	E	120	0,062	0,074	0,087	0,099	0,112
Magnesium, magnesium alloys	< 280 N/mm²	E	400	0,057	0,068	0,080	0,091	0,103
Copper, low-alloy	< 350 N/mm²	E	120	0,062	0,074	0,087	0,099	0,112
Brass, short-chipping	< 600 N/mm²	-	100	0,062	0,074	0,087	0,099	0,112
Brass, long-chipping	< 600 N/mm²	-	100	0,062	0,074	0,087	0,099	0,112
Bronze, short-chipping	< 600 N/mm²	-	100	0,062	0,074	0,087	0,099	0,112
Bronze, short-chipping	650-850 N/mm²	-	80	0,062	0,074	0,087	0,099	0,112
Bronze, long-chipping	< 850 N/mm²	E	80	0,062	0,074	0,087	0,099	0,112
Bronze, long-chipping	850-1200 N/mm²	E	65	0,068	0,082	0,095	0,109	0,122

Legend
E = emulsion
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/t]
The suggested cutting values are reference values and must be adapted to the respective conditions.