HSCo8 end mill, short DIN 844K - ENDMIL-DIN844K-HSCO8-N-D6,0MM

HSCo8 end mill, short DIN 844K

Name: HSCo8 end mill, short DIN 844K
Brand: Würth
SKU: 5443600443

End mill HSCo8 DIN 844K Z4-6 2xD type N
ENDMIL-DIN844K-HSCO8-N-D6,0MM

Art.-no. 5443600443

EAN 4055375875957

All versions

Similar products

Prices for customers after login

HSCo8 end mill, short DIN 844K

Art.-no. 5443600443

Prices for customers after login

Quantity

x 1 pcs

Exclusively for trade customers

Login/Register
Call customer service:

For finishing of steels of average to high strength of up to 1,300 N/mm² with high cutting performance yet good surface properties. Especially for synchronous milling. E.g. construction steels, case-hardened steels and tempering steels, non-ferrous metals, rust and acid-resistant steels.

Notice

Ø 40 mm does not correspond to DIN

Product information

Würth Catalogue

Datasheets(X)

Certificates/ Documents


Product code	1616
Material to be processed	Steel, Cast metal, Stainless steel, Titanium, Copper, Brass, Aluminium, Plastic
Diameter (d1)	6 mm
Shank diameter (d2)	6 mm
Length (l1)	57 mm
Cutting edge length (l2)	13 mm
Number of cutting edges (Z)	4 PCS
Standards	DIN 844
Construction length	Short
Shank style	Cylindrical DIN 1835-B
Cutting material	HSCo8
Surface	Plain
Coolant supply	External
Twist angle	40°
Tolerance of cutting edge diameter	k10
Tolerance of shank diameter	h6
Material of sub-group	General structural steels, Non-alloyed tempering steels < 1000 N/mm², Alloyed tempering steels < 1000 N/mm², Nitriding steels < 1300 N/mm², Grey cast iron, Malleable cast iron, Stainless steels < 850 N/mm², Stainless steels > 850 N/mm², Titanium, Titanium alloys, Copper, Brass, Aluminium, Plastics

Cutting values for finishing contour
For dia. 4 to dia. 15.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 4-5.9	Dia. 6-7.9	Dia. 8-9.9	Dia. 10-11.9	Dia. 12-15.9
General structural steels	< 500 N/mm²	E	45	0,005	0,007	0,010	0,016	0,022
General structural steels	500-850 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
Carbon steels	< 850 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
Carbon steels	850-1000 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
	700-850 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
	850-1000 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,005	0,007	0,010	0,016	0,022
Unalloyed case-hardening steels	< 750 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,005	0,007	0,010	0,016	0,022
Nitriding steels	< 1000 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Nitriding steels	1000-1200 N/mm²	E	25	0,005	0,007	0,010	0,016	0,022
Tool steels	< 850 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
	850-1100 N/mm²	E	25	0,005	0,007	0,010	0,016	0,022
	1100-1400 N/mm²	E	20	0,005	0,007	0,010	0,016	0,022
High-speed steels	850-1200 N/mm²	E	20	0,005	0,007	0,010	0,016	0,022
Wear-resistant constructional steel	1350 N/mm²	E	15	0,005	0,007	0,010	0,016	0,022
Spring steels	< 1200 N/mm²	E	15	0,005	0,007	0,010	0,016	0,022
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
Stainless steels, austenitic	< 700 N/mm²	E	38	0,004	0,006	0,009	0,014	0,019
Stainless steels, austenitic	< 850 N/mm²	E	30	0,004	0,006	0,009	0,014	0,019
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,005	0,007	0,010	0,016	0,022
Special alloys	< 1200 N/mm²	E	15	0,005	0,007	0,010	0,016	0,022
Cast iron	< 180 HB	-	38	0,004	0,006	0,009	0,014	0,019
Cast iron	> 180 HB	-	30	0,004	0,006	0,009	0,014	0,019
Nodular graphite, malleable iron	> 180 HB	-	30	0,004	0,006	0,009	0,014	0,019
Nodular graphite, malleable iron	> 260 HB	E	25	0,004	0,006	0,009	0,014	0,019
Titanium, titanium alloys	< 850 N/mm²	E	20	0,005	0,007	0,010	0,016	0,022
Copper, low-alloy	< 350 N/mm²	E	120	0,008	0,011	0,020	0,029	0,036
Brass, short-chipping	< 600 N/mm²	-	100	0,008	0,011	0,020	0,029	0,036
Brass, long-chipping	< 600 N/mm²	-	100	0,008	0,011	0,020	0,029	0,036
Bronze, short-chipping	< 600 N/mm²	-	100	0,008	0,011	0,020	0,029	0,036
Bronze, short-chipping	650-850 N/mm²	-	80	0,008	0,011	0,020	0,029	0,036
Bronze, long-chipping	< 850 N/mm²	E	80	0,008	0,011	0,020	0,029	0,036
Bronze, long-chipping	850-1200 N/mm²	E	65	0,011	0,014	0,023	0,036	0,041

Legend
E = emulsion		a_e = 0.5xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/t]		a_p = 1xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions.

Cutting values for roughing contour
For dia. 16 to dia. 40
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 16-19.9	Dia. 20-23.9	Dia. 24-31.9	Dia. 32-40
General structural steels	< 500 N/mm²	E	37	0,050	0,063	0,078	0,100
General structural steels	500-850 N/mm²	E	30	0,044	0,056	0,069	0,088
Carbon steels	< 850 N/mm²	E	34	0,044	0,056	0,069	0,088
Carbon steels	850-1000 N/mm²	E	26	0,044	0,056	0,069	0,088
Unalloyed heat-treated steels	< 700 N/mm²	E	33	0,044	0,056	0,069	0,088
	700-850 N/mm²	E	30	0,044	0,056	0,069	0,088
	850-1000 N/mm²	E	24	0,044	0,056	0,069	0,088
Alloyed heat-treated steels	850-1000 N/mm²	E	22	0,044	0,056	0,069	0,088
Alloyed heat-treated steels	1000-1200 N/mm²	E	18	0,050	0,063	0,078	0,100
Unalloyed case-hardening steels	< 750 N/mm²	E	30	0,044	0,056	0,069	0,088
Alloyed case-hardening steels	< 1000 N/mm²	E	22	0,044	0,056	0,069	0,088
Alloyed case-hardening steels	1000-1200 N/mm²	E	18	0,050	0,063	0,078	0,100
Nitriding steels	< 1000 N/mm²	E	22	0,044	0,056	0,069	0,088
Nitriding steels	1000-1200 N/mm²	E	18	0,050	0,063	0,078	0,100
Tool steels	< 850 N/mm²	E	26	0,044	0,056	0,069	0,088
	850-1100 N/mm²	E	16	0,050	0,063	0,078	0,100
	1100-1400 N/mm²	E	9	0,050	0,063	0,078	0,100
High-speed steels	850-1200 N/mm²	E	8	0,050	0,063	0,078	0,100
Wear-resistant constructional steel	1350 N/mm²	E	9	0,050	0,063	0,078	0,100
Spring steels	< 1200 N/mm²	E	8	0,050	0,063	0,078	0,100
Stainless steels, sulphurated	< 700 N/mm²	E	24	0,044	0,056	0,069	0,088
Stainless steels, austenitic	< 700 N/mm²	E	18	0,044	0,056	0,069	0,088
Stainless steels, austenitic	< 850 N/mm²	E	12	0,044	0,056	0,069	0,088
Stainless steels, martensitic	< 1100 N/mm²	E	9	0,050	0,063	0,078	0,100
Special alloys	< 1200 N/mm²	E	7	0,050	0,063	0,078	0,100
Cast iron	< 180 HB	-	34	0,044	0,056	0,069	0,088
Cast iron	> 180 HB	-	30	0,044	0,056	0,069	0,088
Nodular graphite, malleable iron	> 180 HB	-	26	0,044	0,056	0,069	0,088
Nodular graphite, malleable iron	> 260 HB	E	18	0,044	0,056	0,069	0,088
Titanium, titanium alloys	< 850 N/mm²	E	9	0,050	0,063	0,078	0,100
Copper, low-alloy	< 350 N/mm²	E	73	0,078	0,099	0,122	0,157
Brass, short-chipping	< 600 N/mm²	-	73	0,078	0,099	0,122	0,157
Brass, long-chipping	< 600 N/mm²	-	49	0,078	0,099	0,122	0,157
Bronze, short-chipping	< 600 N/mm²	-	49	0,078	0,099	0,122	0,157
Bronze, short-chipping	650-850 N/mm²	-	37	0,078	0,099	0,122	0,157
Bronze, long-chipping	< 850 N/mm²	E	30	0,078	0,099	0,122	0,157
Bronze, long-chipping	850-1200 N/mm²	E	18	0,085	0,107	0,133	0,170

Cutting values for roughing groove
For dia. 12 - dia. 20
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 12-15.9	Dia. 16-19.9	Dia. 20
General structural steels	< 500 N/mm²	E	28	0,025	0,028	0,035
General structural steels	500-850 N/mm²	E	23	0,021	0,025	0,031
Carbon steels	< 850 N/mm²	E	26	0,021	0,025	0,031
Carbon steels	850-1000 N/mm²	E	20	0,021	0,025	0,031
Unalloyed heat-treated steels	< 700 N/mm²	E	25	0,021	0,025	0,031
	700-850 N/mm²	E	23	0,021	0,025	0,031
	850-1000 N/mm²	E	18	0,021	0,025	0,031
Alloyed heat-treated steels	850-1000 N/mm²	E	17	0,021	0,025	0,031
Alloyed heat-treated steels	1000-1200 N/mm²	E	14	0,025	0,028	0,035
Unalloyed case-hardening steels	< 750 N/mm²	E	23	0,021	0,025	0,031
Alloyed case-hardening steels	< 1000 N/mm²	E	17	0,021	0,025	0,031
Alloyed case-hardening steels	1000-1200 N/mm²	E	14	0,025	0,028	0,035
Nitriding steels	< 1000 N/mm²	E	17	0,021	0,025	0,031
Nitriding steels	1000-1200 N/mm²	E	14	0,025	0,028	0,035
Tool steels	< 850 N/mm²	E	20	0,021	0,025	0,031
	850-1100 N/mm²	E	12	0,025	0,028	0,035
	1100-1400 N/mm²	E	7	0,025	0,028	0,035
High-speed steels	850-1200 N/mm²	E	6	0,025	0,028	0,035
Wear-resistant constructional steel	1350 N/mm²	E	7	0,025	0,028	0,035
Spring steels	< 1200 N/mm²	E	6	0,025	0,028	0,035
Stainless steels, sulphurated	< 700 N/mm²	E	18	0,021	0,025	0,031
Stainless steels, austenitic	< 700 N/mm²	E	14	0,021	0,025	0,031
Stainless steels, austenitic	< 850 N/mm²	E	9	0,021	0,025	0,031
Stainless steels, martensitic	< 1100 N/mm²	E	7	0,025	0,028	0,035
Special alloys	< 1200 N/mm²	E	5	0,025	0,028	0,035
Cast iron	< 180 HB	-	26	0,021	0,025	0,031
Cast iron	> 180 HB	-	23	0,021	0,025	0,031
Nodular graphite, malleable iron	> 180 HB	-	20	0,021	0,025	0,031
Nodular graphite, malleable iron	> 260 HB	E	14	0,021	0,025	0,031
Titanium, titanium alloys	< 850 N/mm²	E	7	0,025	0,028	0,035
Copper, low-alloy	< 350 N/mm²	E	55	0,041	0,046	0,055
Brass, short-chipping	< 600 N/mm²	-	55	0,041	0,046	0,055
Brass, long-chipping	< 600 N/mm²	-	37	0,041	0,046	0,055
Bronze, short-chipping	< 600 N/mm²	-	37	0,041	0,046	0,055
Bronze, short-chipping	650-850 N/mm²	-	28	0,041	0,046	0,055
Bronze, long-chipping	< 850 N/mm²	E	23	0,041	0,046	0,055
Bronze, long-chipping	850-1200 N/mm²	E	14	0,045	0,050	0,060

Cutting values for roughing groove
For dia. 4 to dia. 11.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 4-5.9	Dia. 6-7.9	Dia. 8-9.9	Dia. 10-11.9
General structural steels	< 500 N/mm²	E	28	0,005	0,007	0,010	0,016
General structural steels	500-850 N/mm²	E	23	0,004	0,006	0,009	0,014
Carbon steels	< 850 N/mm²	E	26	0,004	0,006	0,009	0,014
Carbon steels	850-1000 N/mm²	E	20	0,004	0,006	0,009	0,014
Unalloyed heat-treated steels	< 700 N/mm²	E	25	0,004	0,006	0,009	0,014
	700-850 N/mm²	E	23	0,004	0,006	0,009	0,014
	850-1000 N/mm²	E	18	0,004	0,006	0,009	0,014
Alloyed heat-treated steels	850-1000 N/mm²	E	17	0,004	0,006	0,009	0,014
Alloyed heat-treated steels	1000-1200 N/mm²	E	14	0,005	0,007	0,010	0,016
Unalloyed case-hardening steels	< 750 N/mm²	E	23	0,004	0,006	0,009	0,014
Alloyed case-hardening steels	< 1000 N/mm²	E	17	0,004	0,006	0,009	0,014
Alloyed case-hardening steels	1000-1200 N/mm²	E	14	0,005	0,007	0,010	0,016
Nitriding steels	< 1000 N/mm²	E	17	0,004	0,006	0,009	0,014
Nitriding steels	1000-1200 N/mm²	E	14	0,005	0,007	0,010	0,016
Tool steels	< 850 N/mm²	E	20	0,004	0,006	0,009	0,014
	850-1100 N/mm²	E	12	0,005	0,007	0,010	0,016
	1100-1400 N/mm²	E	7	0,005	0,007	0,010	0,016
High-speed steels	850-1200 N/mm²	E	6	0,005	0,007	0,010	0,016
Wear-resistant constructional steel	1350 N/mm²	E	7	0,005	0,007	0,010	0,016
Spring steels	< 1200 N/mm²	E	6	0,005	0,007	0,010	0,016
Stainless steels, sulphurated	< 700 N/mm²	E	18	0,004	0,006	0,009	0,014
Stainless steels, austenitic	< 700 N/mm²	E	14	0,004	0,006	0,009	0,014
Stainless steels, austenitic	< 850 N/mm²	E	9	0,004	0,006	0,009	0,014
Stainless steels, martensitic	< 1100 N/mm²	E	7	0,005	0,007	0,010	0,016
Special alloys	< 1200 N/mm²	E	5	0,005	0,007	0,010	0,016
Cast iron	< 180 HB	-	26	0,004	0,006	0,009	0,014
Cast iron	> 180 HB	-	23	0,004	0,006	0,009	0,014
Nodular graphite, malleable iron	> 180 HB	-	20	0,004	0,006	0,009	0,014
Nodular graphite, malleable iron	> 260 HB	E	14	0,004	0,006	0,009	0,014
Titanium, titanium alloys	< 850 N/mm²	E	7	0,005	0,007	0,010	0,016
Copper, low-alloy	< 350 N/mm²	E	55	0,008	0,011	0,020	0,029
Brass, short-chipping	< 600 N/mm²	-	55	0,008	0,011	0,020	0,029
Brass, long-chipping	< 600 N/mm²	-	37	0,008	0,011	0,020	0,029
Bronze, short-chipping	< 600 N/mm²	-	37	0,008	0,011	0,020	0,029
Bronze, short-chipping	650-850 N/mm²	-	28	0,008	0,011	0,020	0,029
Bronze, long-chipping	< 850 N/mm²	E	23	0,008	0,011	0,020	0,029
Bronze, long-chipping	850-1200 N/mm²	E	14	0,011	0,014	0,023	0,036

Cutting values for roughing contour
For dia. 4 to dia. 15.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 4-5.9	Dia. 6-7.9	Dia. 8.0-9.9	Dia. 10-11.9	Dia. 12-15.9
General structural steels	< 500 N/mm²	E	37	0,009	0,017	0,023	0,031	0,037
General structural steels	500-850 N/mm²	E	30	0,007	0,014	0,020	0,027	0,032
Carbon steels	< 850 N/mm²	E	34	0,007	0,014	0,020	0,027	0,032
Carbon steels	850-1000 N/mm²	E	26	0,007	0,014	0,020	0,027	0,032
Unalloyed heat-treated steels	< 700 N/mm²	E	33	0,007	0,014	0,020	0,027	0,032
	700-850 N/mm²	E	30	0,007	0,014	0,020	0,027	0,032
	850-1000 N/mm²	E	24	0,007	0,014	0,020	0,027	0,032
Alloyed heat-treated steels	850-1000 N/mm²	E	22	0,007	0,014	0,020	0,027	0,032
Alloyed heat-treated steels	1000-1200 N/mm²	E	18	0,009	0,017	0,023	0,031	0,037
Unalloyed case-hardening steels	< 750 N/mm²	E	30	0,007	0,014	0,020	0,027	0,032
Alloyed case-hardening steels	< 1000 N/mm²	E	22	0,007	0,014	0,020	0,027	0,032
Alloyed case-hardening steels	1000-1200 N/mm²	E	18	0,009	0,017	0,023	0,031	0,037
Nitriding steels	< 1000 N/mm²	E	22	0,007	0,014	0,020	0,027	0,032
Nitriding steels	1000-1200 N/mm²	E	18	0,009	0,017	0,023	0,031	0,037
Tool steels	< 850 N/mm²	E	26	0,007	0,014	0,020	0,027	0,032
	850-1100 N/mm²	E	16	0,009	0,017	0,023	0,031	0,037
	1100-1400 N/mm²	E	9	0,009	0,017	0,023	0,031	0,037
High-speed steels	850-1200 N/mm²	E	8	0,009	0,017	0,023	0,031	0,037
Wear-resistant constructional steel	1350 N/mm²	E	9	0,009	0,017	0,023	0,031	0,037
Spring steels	< 1200 N/mm²	E	8	0,009	0,017	0,023	0,031	0,037
Stainless steels, sulphurated	< 700 N/mm²	E	24	0,007	0,014	0,020	0,027	0,032
Stainless steels, austenitic	< 700 N/mm²	E	18	0,007	0,014	0,020	0,027	0,032
Stainless steels, austenitic	< 850 N/mm²	E	12	0,007	0,014	0,020	0,027	0,032
Stainless steels, martensitic	< 1100 N/mm²	E	9	0,009	0,017	0,023	0,031	0,037
Special alloys	< 1200 N/mm²	E	7	0,009	0,017	0,023	0,031	0,037
Cast iron	< 180 HB	-	34	0,007	0,014	0,020	0,027	0,032
Cast iron	> 180 HB	-	30	0,007	0,014	0,020	0,027	0,032
Nodular graphite, malleable iron	> 180 HB	-	26	0,007	0,014	0,020	0,027	0,032
Nodular graphite, malleable iron	> 260 HB	E	18	0,007	0,014	0,020	0,027	0,032
Titanium, titanium alloys	< 850 N/mm²	E	9	0,009	0,017	0,023	0,031	0,037
Copper, low-alloy	< 350 N/mm²	E	73	0,014	0,027	0,045	0,057	0,062
Brass, short-chipping	< 600 N/mm²	-	73	0,014	0,027	0,045	0,057	0,062
Brass, long-chipping	< 600 N/mm²	-	49	0,014	0,027	0,045	0,057	0,062
Bronze, short-chipping	< 600 N/mm²	-	49	0,014	0,027	0,045	0,057	0,062
Bronze, short-chipping	650-850 N/mm²	-	37	0,014	0,027	0,045	0,057	0,062
Bronze, long-chipping	< 850 N/mm²	E	30	0,014	0,027	0,045	0,057	0,062
Bronze, long-chipping	850-1200 N/mm²	E	18	0,018	0,034	0,053	0,070	0,069

Legend
E = emulsion		a_e = 1xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/t]		a_p = 1xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions. Full grooves are not possible for diameters greater than 20 mm, as the power consumed is too high.

Legend
E = emulsion		a_e = 0.1xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/t]		a_p = 1.5xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions.

Cutting values for finishing contour
For dia. 16 to dia. 40
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 16-19.9	Dia. 20-23.9	Dia. 24-31.9	Dia. 32-40
General structural steels	< 500 N/mm²	E	45	0,035	0,044	0,057	0,080
General structural steels	500-850 N/mm²	E	38	0,031	0,039	0,050	0,069
Carbon steels	< 850 N/mm²	E	38	0,025	0,031	0,035	0,048
Carbon steels	850-1000 N/mm²	E	30	0,025	0,031	0,035	0,048
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,025	0,031	0,035	0,048
	700-850 N/mm²	E	38	0,025	0,031	0,035	0,048
	850-1000 N/mm²	E	30	0,025	0,031	0,035	0,048
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,025	0,031	0,035	0,048
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,028	0,035	0,040	0,054
Unalloyed case-hardening steels	< 750 N/mm²	E	38	0,025	0,031	0,035	0,048
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,025	0,031	0,035	0,048
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,028	0,035	0,040	0,054
Nitriding steels	< 1000 N/mm²	E	30	0,025	0,031	0,035	0,048
Nitriding steels	1000-1200 N/mm²	E	25	0,028	0,035	0,040	0,054
Tool steels	< 850 N/mm²	E	38	0,025	0,031	0,035	0,048
	850-1100 N/mm²	E	25	0,028	0,035	0,040	0,054
	1100-1400 N/mm²	E	20	0,028	0,035	0,040	0,054
High-speed steels	850-1200 N/mm²	E	20	0,028	0,042	0,048	0,064
Wear-resistant constructional steel	1350 N/mm²	E	15	0,028	0,035	0,040	0,054
Spring steels	< 1200 N/mm²	E	15	0,028	0,035	0,040	0,054
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,025	0,031	0,035	0,048
Stainless steels, austenitic	< 700 N/mm²	E	38	0,025	0,031	0,035	0,048
Stainless steels, austenitic	< 850 N/mm²	E	30	0,025	0,031	0,035	0,048
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,028	0,035	0,040	0,054
Special alloys	< 1200 N/mm²	E	15	0,028	0,035	0,040	0,054
Cast iron	< 180 HB	-	38	0,025	0,031	0,035	0,048
Cast iron	> 180 HB	-	30	0,025	0,031	0,035	0,048
Nodular graphite, malleable iron	> 180 HB	-	30	0,025	0,031	0,035	0,048
Nodular graphite, malleable iron	> 260 HB	E	25	0,025	0,031	0,035	0,048
Titanium, titanium alloys	< 850 N/mm²	E	20	0,028	0,035	0,040	0,054
Copper, low-alloy	< 350 N/mm²	E	120	0,046	0,055	0,062	0,084
Brass, short-chipping	< 600 N/mm²	-	100	0,046	0,055	0,062	0,084
Brass, long-chipping	< 600 N/mm²	-	100	0,046	0,055	0,062	0,084
Bronze, short-chipping	< 600 N/mm²	-	100	0,046	0,055	0,062	0,084
Bronze, short-chipping	650-850 N/mm²	-	80	0,046	0,055	0,062	0,084
Bronze, long-chipping	< 850 N/mm²	E	80	0,046	0,055	0,062	0,084
Bronze, long-chipping	850-1200 N/mm²	E	65	0,050	0,060	0,068	0,092