HSCo8 end mill, short, centre-cutting DIN 844K - ENDMIL-DIN844K-HSCO8-D2,0MM

HSCo8 end mill, short, centre-cutting DIN 844K

Name: HSCo8 end mill, short, centre-cutting DIN 844K
Brand: Würth
SKU: 5443600601

End mill HSCo8 DIN 844K Z3-6 2xD type N
ENDMIL-DIN844K-HSCO8-D2,0MM

Art.-no. 5443600601

EAN 4055375877043

All versions

Similar products

Prices for customers after login

HSCo8 end mill, short, centre-cutting DIN 844K

Art.-no. 5443600601

Prices for customers after login

Quantity

x 1 pcs

Exclusively for trade customers

Login/Register
Call customer service:

Wide range of applications for low-strength materials, yet also difficult-to-machine materials including of high strength, e.g. constructions steels through to tool steels. Also suitable, however, for non-ferrous metals, cobalt and nickel alloys, titanium and titanium alloys.

Product information

Würth Catalogue

Datasheets(X)

Certificates/ Documents


Product code	1816
Material to be processed	Steel, Cast metal, Stainless steel, Titanium, Copper, Brass, Plastic
Diameter (d1)	2 mm
Shank diameter (d2)	6 mm
Length (l1)	51 mm
Cutting edge length (l2)	7 mm
Number of cutting edges (Z)	3 PCS
Standards	DIN 844
Construction length	Short
Shank style	Cylindrical DIN 1835-B
Cutting material	HSCo8
Surface	Plain
Coolant supply	External
Twist angle	30°
Tolerance of cutting edge diameter	k10
Tolerance of shank diameter	h6
Material of sub-group	General structural steels, Non-alloyed tempering steels < 1000 N/mm², Alloyed tempering steels < 1000 N/mm², Nitriding steels < 1300 N/mm², Grey cast iron, Malleable cast iron, Stainless steels < 850 N/mm², Stainless steels > 850 N/mm², Titanium, Titanium alloys, Copper, Brass, Plastics

Cutting values for finishing contour
For dia. 2 to dia. 11.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 2-3.9	Dia. 4-5.9	Dia. 6-7.9	Dia. 8-9.9	Dia. 10-11.9
General structural steels	< 500 N/mm²	E	45	0,003	0,005	0,007	0,010	0,016
General structural steels	500-850 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
Machining steels	< 850 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
Machining steels	850-1000 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
	700-850 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
	850-1000 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,003	0,005	0,007	0,010	0,016
Non-alloyed case-hardening steels	< 750 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,003	0,005	0,007	0,010	0,016
Nitriding steels	< 1000 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Nitriding steels	1000-1200 N/mm²	E	25	0,003	0,005	0,007	0,010	0,016
Tool steels	< 850 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
	850-1100 N/mm²	E	25	0,003	0,005	0,007	0,010	0,016
	1100-1400 N/mm²	E	20	0,003	0,005	0,007	0,010	0,016
High-speed steels	850-1200 N/mm²	E	20	0,003	0,005	0,007	0,010	0,016
Wear-resistant constructional steel	1350 N/mm²	E	15	0,003	0,005	0,007	0,010	0,016
Spring steels	< 1200 N/mm²	E	15	0,003	0,005	0,007	0,010	0,016
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
Stainless steels, austenitic	< 700 N/mm²	E	38	0,003	0,004	0,006	0,009	0,014
Stainless steels, austenitic	< 850 N/mm²	E	30	0,003	0,004	0,006	0,009	0,014
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,003	0,005	0,007	0,010	0,016
Cast iron	< 180 HB	-	38	0,003	0,004	0,006	0,009	0,014
Cast iron	> 180 HB	-	30	0,003	0,004	0,006	0,009	0,014
Spheroidal graphite, malleable iron	> 180 HB	-	30	0,003	0,004	0,006	0,009	0,014
Spheroidal graphite, malleable iron	> 260 HB	E	25	0,003	0,004	0,006	0,009	0,014
Titanium, titanium alloys	< 850 N/mm²	E	20	0,003	0,005	0,007	0,010	0,016
Copper, low-alloy	< 350 N/mm²	E	120	0,006	0,008	0,011	0,020	0,029
Brass, short-chipping	< 600 N/mm²	-	100	0,006	0,008	0,011	0,020	0,029
Brass, long-chipping	< 600 N/mm²	-	100	0,006	0,008	0,011	0,020	0,029
Bronze, short-chipping	< 600 N/mm²	-	100	0,006	0,008	0,011	0,020	0,029
Bronze, short-chipping	650-850 N/mm²	-	80	0,006	0,008	0,011	0,020	0,029
Bronze, long-chipping	< 850 N/mm²	E	80	0,006	0,008	0,011	0,020	0,029
Bronze, long-chipping	850-1200 N/mm²	E	65	0,006	0,011	0,014	0,023	0,036

Legend
E = emulsion		a_e = 0.5xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/z]		a_p = 1xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions.

Cutting values for roughing contour
For dia. 12 to dia. 32
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 12-15.9	Dia. 16-19.9	Dia. 20-23.9	Dia. 24-31.9	Dia. 32
General structural steels	< 500 N/mm²	E	37	0,037	0,050	0,063	0,078	0,100
General structural steels	500-850 N/mm²	E	30	0,032	0,044	0,056	0,069	0,088
Machining steels	< 850 N/mm²	E	34	0,032	0,044	0,056	0,069	0,088
Machining steels	850-1000 N/mm²	E	26	0,032	0,044	0,056	0,069	0,088
Unalloyed heat-treated steels	< 700 N/mm²	E	33	0,032	0,044	0,056	0,069	0,088
	700-850 N/mm²	E	30	0,032	0,044	0,056	0,069	0,088
	850-1000 N/mm²	E	24	0,032	0,044	0,056	0,069	0,088
Alloyed heat-treated steels	850-1000 N/mm²	E	22	0,032	0,044	0,056	0,069	0,088
Alloyed heat-treated steels	1000-1200 N/mm²	E	18	0,037	0,050	0,063	0,078	0,100
Non-alloyed case-hardening steels	< 750 N/mm²	E	30	0,032	0,044	0,056	0,069	0,088
Alloyed case-hardening steels	< 1000 N/mm²	E	22	0,032	0,044	0,056	0,069	0,088
Alloyed case-hardening steels	1000-1200 N/mm²	E	18	0,037	0,050	0,063	0,078	0,100
Nitriding steels	< 1000 N/mm²	E	22	0,032	0,044	0,056	0,069	0,088
Nitriding steels	1000-1200 N/mm²	E	18	0,037	0,050	0,063	0,078	0,100
Tool steels	< 850 N/mm²	E	26	0,032	0,044	0,056	0,069	0,088
	850-1100 N/mm²	E	16	0,037	0,050	0,063	0,078	0,100
	1100-1400 N/mm²	E	9	0,037	0,050	0,063	0,078	0,100
High-speed steels	850-1200 N/mm²	E	8	0,037	0,050	0,063	0,078	0,100
Wear-resistant constructional steel	1350 N/mm²	E	9	0,037	0,050	0,063	0,078	0,100
Spring steels	< 1200 N/mm²	E	8	0,037	0,050	0,063	0,078	0,100
Stainless steels, sulphurated	< 700 N/mm²	E	24	0,032	0,044	0,056	0,069	0,088
Stainless steels, austenitic	< 700 N/mm²	E	18	0,032	0,044	0,056	0,069	0,088
Stainless steels, austenitic	< 850 N/mm²	E	12	0,032	0,044	0,056	0,069	0,088
Stainless steels, martensitic	< 1100 N/mm²	E	9	0,037	0,050	0,063	0,078	0,100
Cast iron	< 180 HB	-	34	0,032	0,044	0,056	0,069	0,088
Cast iron	> 180 HB	-	30	0,032	0,044	0,056	0,069	0,088
Spheroidal graphite, malleable iron	> 180 HB	-	26	0,032	0,044	0,056	0,069	0,088
Spheroidal graphite, malleable iron	> 260 HB	E	18	0,032	0,044	0,056	0,069	0,088
Titanium, titanium alloys	< 850 N/mm²	E	9	0,037	0,050	0,063	0,078	0,100
Copper, low-alloy	< 350 N/mm²	E	73	0,062	0,078	0,099	0,122	0,157
Brass, short-chipping	< 600 N/mm²	-	73	0,062	0,078	0,099	0,122	0,157
Brass, long-chipping	< 600 N/mm²	-	49	0,062	0,078	0,099	0,122	0,157
Bronze, short-chipping	< 600 N/mm²	-	49	0,062	0,078	0,099	0,122	0,157
Bronze, short-chipping	650-850 N/mm²	-	37	0,062	0,078	0,099	0,122	0,157
Bronze, long-chipping	< 850 N/mm²	E	30	0,062	0,078	0,099	0,122	0,157
Bronze, long-chipping	850-1200 N/mm²	E	18	0,069	0,085	0,107	0,133	0,170

Cutting values for roughing groove
For dia. 10 to dia. 20
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 10-11.9	Dia. 12-15.9	Dia. 16-19.9	Dia. 20
General structural steels	< 500 N/mm²	E	28	0,016	0,025	0,028	0,035
General structural steels	500-850 N/mm²	E	23	0,014	0,021	0,025	0,031
Machining steels	< 850 N/mm²	E	26	0,014	0,021	0,025	0,031
Machining steels	850-1000 N/mm²	E	20	0,014	0,021	0,025	0,031
Unalloyed heat-treated steels	< 700 N/mm²	E	25	0,014	0,021	0,025	0,031
	700-850 N/mm²	E	23	0,014	0,021	0,025	0,031
	850-1000 N/mm²	E	18	0,014	0,021	0,025	0,031
Alloyed heat-treated steels	850-1000 N/mm²	E	17	0,014	0,021	0,025	0,031
Alloyed heat-treated steels	1000-1200 N/mm²	E	14	0,016	0,025	0,028	0,035
Non-alloyed case-hardening steels	< 750 N/mm²	E	23	0,014	0,021	0,025	0,031
Alloyed case-hardening steels	< 1000 N/mm²	E	17	0,014	0,021	0,025	0,031
Alloyed case-hardening steels	1000-1200 N/mm²	E	14	0,016	0,025	0,028	0,035
Nitriding steels	< 1000 N/mm²	E	17	0,014	0,021	0,025	0,031
Nitriding steels	1000-1200 N/mm²	E	14	0,016	0,025	0,028	0,035
Tool steels	< 850 N/mm²	E	20	0,014	0,021	0,025	0,031
	850-1100 N/mm²	E	12	0,016	0,025	0,028	0,035
	1100-1400 N/mm²	E	7	0,016	0,025	0,028	0,035
High-speed steels	850-1200 N/mm²	E	6	0,016	0,025	0,028	0,035
Wear-resistant constructional steel	1350 N/mm²	E	7	0,016	0,025	0,028	0,035
Spring steels	< 1200 N/mm²	E	6	0,016	0,025	0,028	0,035
Stainless steels, sulphurated	< 700 N/mm²	E	18	0,014	0,021	0,025	0,031
Stainless steels, austenitic	< 700 N/mm²	E	14	0,014	0,021	0,025	0,031
Stainless steels, austenitic	< 850 N/mm²	E	9	0,014	0,021	0,025	0,031
Stainless steels, martensitic	< 1100 N/mm²	E	7	0,016	0,025	0,028	0,035
Cast iron	< 180 HB	-	26	0,014	0,021	0,025	0,031
Cast iron	> 180 HB	-	23	0,014	0,021	0,025	0,031
Spheroidal graphite, malleable iron	> 180 HB	-	20	0,014	0,021	0,025	0,031
Spheroidal graphite, malleable iron	> 260 HB	E	14	0,014	0,021	0,025	0,031
Titanium, titanium alloys	< 850 N/mm²	E	7	0,016	0,025	0,028	0,035
Copper, low-alloy	< 350 N/mm²	E	55	0,029	0,041	0,046	0,055
Brass, short-chipping	< 600 N/mm²	-	55	0,029	0,041	0,046	0,055
Brass, long-chipping	< 600 N/mm²	-	37	0,029	0,041	0,046	0,055
Bronze, short-chipping	< 600 N/mm²	-	37	0,029	0,041	0,046	0,055
Bronze, short-chipping	650-850 N/mm²	-	28	0,029	0,041	0,046	0,055
Bronze, long-chipping	< 850 N/mm²	E	23	0,029	0,041	0,046	0,055
Bronze, long-chipping	850-1200 N/mm²	E	14	0,036	0,045	0,050	0,060

Cutting values for roughing groove
For dia. 2 to dia. 9.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 2-3.9	Dia. 4-5.9	Dia. 6-7.9	Dia. 8-9.9
General structural steels	< 500 N/mm²	E	28	0,003	0,005	0,007	0,010
General structural steels	500-850 N/mm²	E	23	0,003	0,004	0,006	0,009
Machining steels	< 850 N/mm²	E	26	0,003	0,004	0,006	0,009
Machining steels	850-1000 N/mm²	E	20	0,003	0,004	0,006	0,009
Unalloyed heat-treated steels	< 700 N/mm²	E	25	0,003	0,004	0,006	0,009
	700-850 N/mm²	E	23	0,003	0,004	0,006	0,009
	850-1000 N/mm²	E	18	0,003	0,004	0,006	0,009
Alloyed heat-treated steels	850-1000 N/mm²	E	17	0,003	0,004	0,006	0,009
Alloyed heat-treated steels	1000-1200 N/mm²	E	14	0,003	0,005	0,007	0,010
Non-alloyed case-hardening steels	< 750 N/mm²	E	23	0,003	0,004	0,006	0,009
Alloyed case-hardening steels	< 1000 N/mm²	E	17	0,003	0,004	0,006	0,009
Alloyed case-hardening steels	1000-1200 N/mm²	E	14	0,003	0,005	0,007	0,010
Nitriding steels	< 1000 N/mm²	E	17	0,003	0,004	0,006	0,009
Nitriding steels	1000-1200 N/mm²	E	14	0,003	0,005	0,007	0,010
Tool steels	< 850 N/mm²	E	20	0,003	0,004	0,006	0,009
	850-1100 N/mm²	E	12	0,003	0,005	0,007	0,010
	1100-1400 N/mm²	E	7	0,003	0,005	0,007	0,010
High-speed steels	850-1200 N/mm²	E	6	0,003	0,005	0,007	0,010
Wear-resistant constructional steel	1350 N/mm²	E	7	0,003	0,005	0,007	0,010
Spring steels	< 1200 N/mm²	E	6	0,003	0,005	0,007	0,010
Stainless steels, sulphurated	< 700 N/mm²	E	18	0,003	0,004	0,006	0,009
Stainless steels, austenitic	< 700 N/mm²	E	14	0,003	0,004	0,006	0,009
Stainless steels, austenitic	< 850 N/mm²	E	9	0,003	0,004	0,006	0,009
Stainless steels, martensitic	< 1100 N/mm²	E	7	0,003	0,005	0,007	0,010
Cast iron	< 180 HB	-	26	0,003	0,004	0,006	0,009
Cast iron	> 180 HB	-	23	0,003	0,004	0,006	0,009
Spheroidal graphite, malleable iron	> 180 HB	-	20	0,003	0,004	0,006	0,009
Spheroidal graphite, malleable iron	> 260 HB	E	14	0,003	0,004	0,006	0,009
Titanium, titanium alloys	< 850 N/mm²	E	7	0,003	0,005	0,007	0,010
Copper, low-alloy	< 350 N/mm²	E	55	0,006	0,008	0,011	0,020
Brass, short-chipping	< 600 N/mm²	-	55	0,006	0,008	0,011	0,020
Brass, long-chipping	< 600 N/mm²	-	37	0,006	0,008	0,011	0,020
Bronze, short-chipping	< 600 N/mm²	-	37	0,006	0,008	0,011	0,020
Bronze, short-chipping	650-850 N/mm²	-	28	0,006	0,008	0,011	0,020
Bronze, long-chipping	< 850 N/mm²	E	23	0,006	0,008	0,011	0,020
Bronze, long-chipping	850-1200 N/mm²	E	14	0,006	0,011	0,014	0,023

Cutting values for roughing contour
For dia. 2 to dia. 11.9
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 2-3.9	Dia. 4-5.9	Dia. 6-7.9	Dia. 8.0-9.9	Dia. 10-11.9
General structural steels	< 500 N/mm²	E	37	0,005	0,009	0,017	0,023	0,031
General structural steels	500-850 N/mm²	E	30	0,005	0,007	0,014	0,020	0,027
Machining steels	< 850 N/mm²	E	34	0,005	0,007	0,014	0,020	0,027
Machining steels	850-1000 N/mm²	E	26	0,005	0,007	0,014	0,020	0,027
Unalloyed heat-treated steels	< 700 N/mm²	E	33	0,005	0,007	0,014	0,020	0,027
	700-850 N/mm²	E	30	0,005	0,007	0,014	0,020	0,027
	850-1000 N/mm²	E	24	0,005	0,007	0,014	0,020	0,027
Alloyed heat-treated steels	850-1000 N/mm²	E	22	0,005	0,007	0,014	0,020	0,027
Alloyed heat-treated steels	1000-1200 N/mm²	E	18	0,005	0,009	0,017	0,023	0,031
Non-alloyed case-hardening steels	< 750 N/mm²	E	30	0,005	0,007	0,014	0,020	0,027
Alloyed case-hardening steels	< 1000 N/mm²	E	22	0,005	0,007	0,014	0,020	0,027
Alloyed case-hardening steels	1000-1200 N/mm²	E	18	0,005	0,009	0,017	0,023	0,031
Nitriding steels	< 1000 N/mm²	E	22	0,005	0,007	0,014	0,020	0,027
Nitriding steels	1000-1200 N/mm²	E	18	0,005	0,009	0,017	0,023	0,031
Tool steels	< 850 N/mm²	E	26	0,005	0,007	0,014	0,020	0,027
	850-1100 N/mm²	E	16	0,005	0,009	0,017	0,023	0,031
	1100-1400 N/mm²	E	9	0,005	0,009	0,017	0,023	0,031
High-speed steels	850-1200 N/mm²	E	8	0,005	0,009	0,017	0,023	0,031
Wear-resistant constructional steel	1350 N/mm²	E	9	0,005	0,009	0,017	0,023	0,031
Spring steels	< 1200 N/mm²	E	8	0,005	0,009	0,017	0,023	0,031
Stainless steels, sulphurated	< 700 N/mm²	E	24	0,005	0,007	0,014	0,020	0,027
Stainless steels, austenitic	< 700 N/mm²	E	18	0,005	0,007	0,014	0,020	0,027
Stainless steels, austenitic	< 850 N/mm²	E	12	0,005	0,007	0,014	0,020	0,027
Stainless steels, martensitic	< 1100 N/mm²	E	9	0,005	0,009	0,017	0,023	0,031
Cast iron	< 180 HB	-	34	0,005	0,007	0,014	0,020	0,027
Cast iron	> 180 HB	-	30	0,005	0,007	0,014	0,020	0,027
Spheroidal graphite, malleable iron	> 180 HB	-	26	0,005	0,007	0,014	0,020	0,027
Spheroidal graphite, malleable iron	> 260 HB	E	18	0,005	0,007	0,014	0,020	0,027
Titanium, titanium alloys	< 850 N/mm²	E	9	0,005	0,009	0,017	0,023	0,031
Copper, low-alloy	< 350 N/mm²	E	73	0,010	0,014	0,027	0,045	0,057
Brass, short-chipping	< 600 N/mm²	-	73	0,010	0,014	0,027	0,045	0,057
Brass, long-chipping	< 600 N/mm²	-	49	0,010	0,014	0,027	0,045	0,057
Bronze, short-chipping	< 600 N/mm²	-	49	0,010	0,014	0,027	0,045	0,057
Bronze, short-chipping	650-850 N/mm²	-	37	0,010	0,014	0,027	0,045	0,057
Bronze, long-chipping	< 850 N/mm²	E	30	0,010	0,014	0,027	0,045	0,057
Bronze, long-chipping	850-1200 N/mm²	E	18	0,010	0,018	0,034	0,053	0,070

Legend
E = emulsion		a_e = 1xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/z]		a_p = 1xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions. Full grooves are not possible for diameters greater than 20 mm, as the power consumed is too high.

Legend
E = emulsion		a_e = 0.1xd1
v_c = cutting speed [m/min]
f_z = feed per tooth [mm/z]		a_p = 1.5xd1
a_e = cutting thickness (radial)
a_p = cutting thickness (axial)
The suggested cutting values are reference values and must be adapted to the respective conditions.

Cutting values for finishing contour
For dia. 12 to dia. 32
Material designation	Tensile strength	Cooling	v_c	f_z
				Dia. 12-15.9	Dia. 16-19.9	Dia. 20-23.9	Dia. 24-31.9	Dia. 32
General structural steels	< 500 N/mm²	E	45	0,022	0,035	0,044	0,057	0,080
General structural steels	500-850 N/mm²	E	38	0,019	0,031	0,039	0,050	0,069
Machining steels	< 850 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
Machining steels	850-1000 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Unalloyed heat-treated steels	< 700 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
	700-850 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
	850-1000 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Alloyed heat-treated steels	850-1000 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Alloyed heat-treated steels	1000-1200 N/mm²	E	25	0,022	0,028	0,035	0,040	0,054
Non-alloyed case-hardening steels	< 750 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
Alloyed case-hardening steels	< 1000 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Alloyed case-hardening steels	1000-1200 N/mm²	E	25	0,022	0,028	0,035	0,040	0,054
Nitriding steels	< 1000 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Nitriding steels	1000-1200 N/mm²	E	25	0,022	0,028	0,035	0,040	0,054
Tool steels	< 850 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
	850-1100 N/mm²	E	25	0,022	0,028	0,035	0,040	0,054
	1100-1400 N/mm²	E	20	0,022	0,028	0,035	0,040	0,054
High-speed steels	850-1200 N/mm²	E	20	0,022	0,028	0,042	0,048	0,064
Wear-resistant constructional steel	1350 N/mm²	E	15	0,022	0,028	0,035	0,040	0,054
Spring steels	< 1200 N/mm²	E	15	0,022	0,028	0,035	0,040	0,054
Stainless steels, sulphurated	< 700 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
Stainless steels, austenitic	< 700 N/mm²	E	38	0,019	0,025	0,031	0,035	0,048
Stainless steels, austenitic	< 850 N/mm²	E	30	0,019	0,025	0,031	0,035	0,048
Stainless steels, martensitic	< 1100 N/mm²	E	25	0,022	0,028	0,035	0,040	0,054
Cast iron	< 180 HB	-	38	0,019	0,025	0,031	0,035	0,048
Cast iron	> 180 HB	-	30	0,019	0,025	0,031	0,035	0,048
Spheroidal graphite, malleable iron	> 180 HB	-	30	0,019	0,025	0,031	0,035	0,048
Spheroidal graphite, malleable iron	> 260 HB	E	25	0,019	0,025	0,031	0,035	0,048
Titanium, titanium alloys	< 850 N/mm²	E	20	0,022	0,028	0,035	0,040	0,054
Copper, low-alloy	< 350 N/mm²	E	120	0,036	0,046	0,055	0,062	0,084
Brass, short-chipping	< 600 N/mm²	-	100	0,036	0,046	0,055	0,062	0,084
Brass, long-chipping	< 600 N/mm²	-	100	0,036	0,046	0,055	0,062	0,084
Bronze, short-chipping	< 600 N/mm²	-	100	0,036	0,046	0,055	0,062	0,084
Bronze, short-chipping	650-850 N/mm²	-	80	0,036	0,046	0,055	0,062	0,084
Bronze, long-chipping	< 850 N/mm²	E	80	0,036	0,046	0,055	0,062	0,084
Bronze, long-chipping	850-1200 N/mm²	E	65	0,041	0,050	0,060	0,068	0,092