Parquet acrylic
Acrylic sealant Parquet Acrylic
ACRYSEAL-PARQ-OAK-310ML
Register now and access more than 125,000 products
Flexibility
High absorption of movements.
Sanding
During subsequent sanding work on parquet, parquet acrylic can be sanded without damaging the sealant.
Painting over
Once hardened, can be treated and painted with commercially available parquet sealing products (preliminary testing is required).
Silicone-free
- Neutral silicone perfect should be used for elastic sealing, e.g. of floating parquet, laminate flooring or gap sealing of boarded floors
- Due to the large number of varnish and glazing formulations, preliminary testing is required in order to rule out any interactions
- Care must be taken with sealant joints that have been fully painted over. These tend to develop cracks when movement occurs in the joint, as the applied paint is generally less elastic than the sealant and then causes cracks to form in the paint
- Sufficient air exchange should be ensured during the curing phase
- A higher coating thickness extends the curing time
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
- For sealing indoor connection joints on parquet floors, movement joints in parquet and door frames
- Suitable for parquet flooring, glued over the entire surface, with low expansion properties
- The surface must be dry, capable of bearing load and free from dust, grease and wax
- Loose components, old coatings or paint and sealant residues must be removed prior to application
- Please observe the "General Notes on Application for Sealants" overview sheet. Further information can be found in the technical data sheet.
Colour | Oak |
Contents | 310 ml |
Container | Cartridge |
Chemical basis | Polyacrylic dispersion |
Density | 1.75 g/cm³ |
Continuous motion absorption | 10 % |
Smell/fragrance | Faint odour |
Min. skin-formation time | 10 min |
Shore A hardness | 25 |
Min./max. temperature resistance | -25 to 80 °C |
Min./max. processing temperature | 5 to 40 °C |
Full curing speed | 1 mm/d |
Min. final strength | 28 d |
Can be sanded after | 10 d |
Shelf life from production | 24 Month |
Datasheets(X)
Select RAL-colour code
!! NOTE: On-screen visualisation of the colour differs from real colour shade!!
Last viewed
Solid carbide end mill With Speedcut Universal corner radius, extra-long XXL, optional, four cutting edges, uneven angle of twist gradient
Fastening set for cross beams
Safety boots, S3
Hex head screw with shank ISO 4014, steel 8.8, zinc-plated, blue passivated (A2K)
KALTSCHMELZ® device KSG-E Caravan For adhesive-free insertion of variably positionable plastic anchors into frameless lightweight panels
Print material FFF PETG Material4Print
Feather key, high profile DIN 6885, steel C 45 K, plain, shape A
Twist drill bit HSCo DIN 340 type RN OXIDE
Glazing packer
Hygienic design adjustable foot