Textured acrylic
Textured acrylic
ACRYSEAL-FLEX-STRUCTURE-WHITE-310ML
Register now and access more than 125,000 products
Fine-grained structure
An even grain structure is produced by adding high-quality quartz sand.
- Can be painted over with emulsion paints
- Resistant to UV and ageing
- Odourless
- Not suitable for use in building construction joints in accordance with DIN 18540
- Due to the large number of varnish and glazing formulations, preliminary testing is required in order to rule out any interactions
- Take care with sealant joints that have been fully painted over. These tend to develop cracks when movement occurs in the joint, as the applied paint is generally less elastic than the sealant and then causes cracks to form in the paint.
- The setting speed is dependent on the application temperature, the weather and the surface moisture. The setting speed is greatly delayed in cold, damp weather.
- Discolouration may occur in wood containing tannic acid
Tested in accordance with EN 15651 Part 1
- Fire behaviour: Class E
- Stability under load: ≤ 3 mm
- Volume loss: ≤ 25%
- Tensile behaviour after immersion in water at 23°C (ductile): ≥ 25%
- Durability: Passed
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
- For sealing cracks and damage to plaster, concrete and gypsum
- For sealing structured and textured plaster, both indoors and outdoors
- Adhesion surfaces must be clean, dry and firm
- A primer, e.g. with Silicone primer, improves the adhesion for absorbent or porous surfaces.
- Please observe the "General Notes on Application for Sealants" overview sheet. For more information, please refer to the technical data sheet.
Container | Cartridge |
Contents | 310 ml |
Fungicidal properties | No |
Colour | White |
Chemical basis | Acrylate dispersion |
Density | 1.8 g/cm³ |
Continuous motion absorption | 7.5 % |
Smell/fragrance | Odourless |
Full curing speed | 0.5 mm/d |
Fully hardening/curing conditions | 23°C and 50% relative humidity |
Min. skin-formation time | 5 min |
Min. breaking elongation | 50 % |
Breaking elongation conditions | for 2-mm film |
Conditions for skin-formation time | at 23°C and 50% relative humidity |
Shore A hardness | 28 |
Min./max. temperature resistance | -20 to 75 °C |
Min./max. processing temperature | 5 to 40 °C |
Recoatable/Can be painted over | Yes |
Surface pre-treatment required | On absorbent or porous surfaces |
Mixing ratio | Mixing ratio of acrylic sealant to water = 1:1 to 1:5 |
Ultraviolet resistance | Yes |
Coating compatibility | Yes |
Shelf life from production | 18 Month |
Conditions to maintain shelf life from production | at 10°C to 25°C |
Datasheets(X)
Select RAL-colour code
!! NOTE: On-screen visualisation of the colour differs from real colour shade!!
Last viewed
Safety sandals, S1
Work trousers
Low-cut safety shoes, S1
Useit® Superpad wood sanding disc
Occupational boot O2 Steitz VD PRO 3805 GTX
Anchor point ABS Lock III BE Pro 24
GEFU® thread-rolling screw With Taptite 2000® thread, hexagon head with collar
3KS Plus profile double cylinder For keyed alike profile cylinders in original equipment
HSCo8 end mill, short, triple blade, centre-cutting DIN 844K
Vulcanised fibre disc Aluminium oxide fibre disc with TOP SIZE active grinding layer for machining stainless steel.